Métodos experimentais na determinação das propriedades mecânicas de betões a altas temperaturas
Type
conferenceObject
Creator
Identifier
SANTOS, C.C.; RODRIGUES, J.P.; CAETANO, H. (2014) - Métodos experimentais na determinação das propriedades mecânicas de betões a altas temperaturas. In Congresso Nacional de Mecânica Experimental, 9, Aveiro, 15-17 de Outubro – CNME2014. Aveiro: [Universidade de Aveiro]. 11 p.
Title
Métodos experimentais na determinação das propriedades mecânicas de betões a altas temperaturas
Experimental methods on the determination of the mechanical properties of concrete at high temperatures
Experimental methods on the determination of the mechanical properties of concrete at high temperatures
Subject
Métodos experimentais
Propriedades mecânicas
Betão
Temperaturas elevadas
Propriedades mecânicas
Betão
Temperaturas elevadas
Date
2015-03-23T15:17:42Z
2015-03-23T15:17:42Z
2014-10
2015-03-23T15:17:42Z
2014-10
Description
Até ao momento não existem ainda procedimentos padrão para ensaios a altas temperaturas no betão, pelo que têm sido realizados ensaios a temperaturas elevadas adaptados de ensaios à temperatura ambiente. Os ensaios têm-se dividido entre ensaios a altas temperaturas e residuais após aquecimento e arrefecimento. O primeiro procedimento é mais adequado para a determinação das propriedades mecânicas do betão durante um incêndio enquanto o segundo procedimento é usado para determinar a resistência residual do betão após incêndio. Nesta comunicação apresentam-se os resultados de ensaios realizados por diferentes autores para a determinação das propriedades mecânicas residuais do betão após aquecimento e arrefecimento. Os resultados apresentados dizem respeito a resistências residuais à compressão, tração e flexão e módulo de elasticidade. Os métodos de ensaio aplicados são devidamente descritos e os resultados obtidos são objeto de análises comparativas.
ABSTRACT: So far there are no standard procedures for testing concrete at high temperatures which have been conducted according to the ones at ambient temperature. The tests have been divided between tests at high temperatures and residual after heating and cooling. The first procedure is appropriate for determining the mechanical properties of concrete during fire while the second is used to determine the residual mechanical properties of concrete after fire. In this paper are presented the results of tests carried out by different authors for assessing the residual mechanical properties of concrete after heating and cooling. The results presented are respecting to residual compressive, tensile and flexural strength and elasticity modulus. The test methods are described and results obtained are compared.
ABSTRACT: So far there are no standard procedures for testing concrete at high temperatures which have been conducted according to the ones at ambient temperature. The tests have been divided between tests at high temperatures and residual after heating and cooling. The first procedure is appropriate for determining the mechanical properties of concrete during fire while the second is used to determine the residual mechanical properties of concrete after fire. In this paper are presented the results of tests carried out by different authors for assessing the residual mechanical properties of concrete after heating and cooling. The results presented are respecting to residual compressive, tensile and flexural strength and elasticity modulus. The test methods are described and results obtained are compared.